Physical Review Letters
Author:
Keywords:
Science & Technology, Physical Sciences, Physics, Multidisciplinary, Physics, MAGNESIUM DIFFUSION, IMPLANTATION, REFINEMENT, DEFECTS, SITE, 01 Mathematical Sciences, 02 Physical Sciences, 09 Engineering, General Physics, 40 Engineering, 49 Mathematical sciences, 51 Physical sciences
Abstract:
Radioactive ^{27}Mg (t_{1/2}=9.5 min) was implanted into GaN of different doping types at CERN's ISOLDE facility and its lattice site determined via β^{-} emission channeling. Following implantations between room temperature and 800 °C, the majority of ^{27}Mg occupies the substitutional Ga sites; however, below 350 °C significant fractions were also found on interstitial positions ∼0.6 Å from ideal octahedral sites. The interstitial fraction of Mg was correlated with the GaN doping character, being highest (up to 31%) in samples doped p type with 2×10^{19} cm^{-3} stable Mg during epilayer growth, and lowest in Si-doped n-GaN, thus giving direct evidence for the amphoteric character of Mg. Implanting above 350 °C converts interstitial ^{27}Mg to substitutional Ga sites, which allows estimating the activation energy for migration of interstitial Mg as between 1.3 and 2.0 eV.