Metal-matrix composite, Electrical contact, Infiltration, Contact resistance, Thermal conductivity, Thermal stress cracking, Science & Technology, Technology, Materials Science, Multidisciplinary, Materials Science, TUNGSTEN CARBIDE, YIELD STRENGTH, HARDNESS, NICKEL, ARC, 0910 Manufacturing Engineering, 0912 Materials Engineering, 0913 Mechanical Engineering, Materials, 4016 Materials engineering, 4017 Mechanical engineering

Abstract:

In this work, theoretically dense (> 99%) composites of Ag and WC have been prepared by press–sintering–infiltration for making electrical contacts used as an arc-resistant material in a model switching device. Composites with varying silver content and WC particle size were investigated to get an insight on their electrical contact resistance (Rc) and their ability to withstand enormous thermal stresses during switching. A break-only model switching sequence was used, where the evolution of Rc was measured over 50 cycles and the post-switching microstructures were investigated for thermal stress induced crack formation. A well-established 2D computational microstructure based model, object-oriented finite element analysis version 2 (OOF2), was used to determine the composite thermal conductivity (k) for various grades as a function of temperature. Rc was observed to be consistently low for the coarser WC containing composite and higher silver content composites. This response was attributed to the ductility of the surface layers formed during switching. Crack formation after switching was found to be a direct consequence of large thermal gradients during 50 cycles, which was minimal for coarser WC grained and higher silver content composites which have a higher thermal shock resistance.