Title: The crystal structure of Na-2(UO2)(2)SiO4F2, a compound structurally related to soddyite, and formed during uranyl silicate synthesis in Teflon-lined bombs
Authors: Blaton, Norbert ×
Vochten, R
Peeters, OM
van Springel, K #
Issue Date: Jun-1999
Publisher: E schweizerbartsche verlags
Series Title: Neues jahrbuch fur mineralogie-monatshefte issue:6 pages:253-264
Abstract: During the formation of sodium-boltwoodite from boltwoodite in a Teflon(R) vessel, a new uranyl compound with composition Na-2(UO2)(2)SiO4F2 was formed. The yellow crystals have tetragonal structure, a 6.975(8)Angstrom, c = 18.31(2) Angstrom, V = 891(2) Angstrom(3), D-c = 5.348 g cm(-3), Z = 4, space group I4(1)/amd(No 141). The crystal structure was solved by Patterson methods and refined to an unweighted residual of 0.030, based on 204 observed (F-2 > 4 sigma F-2) reflections measured with MoK alpha X-radiation on a single-crystal diffractometer. The structure is build up of UO6F pentagonal bipyramids which form endless chains by edge sharing. The chains are joined by sharing edges with SiO4 tetrahedra, resulting in a framework structure. Sodium atoms are surrounded by two fluorine and four oxygen atoms. The strongest ten reflections of the X-ray powder pattern [d(Angstrom), (I), hkl] are: 4.599(100)013, 3.492(89)200, 2.599(84)116, 6.53(75)011, 4.348(67)112, 1.791(63) 316, 3.247(59)105, 2.781(57)123, 3.078(37)121 and 1.957(34)109. The infrared spectrum was recorded.
ISSN: 0028-3649
Publication status: published
KU Leuven publication type: IT
Appears in Collections:Biocrystallography
× corresponding author
# (joint) last author

Files in This Item:

There are no files associated with this item.

Request a copy

 




All items in Lirias are protected by copyright, with all rights reserved.

© Web of science