Title: The effect of nitrogen incorporation on the bonding structure of hydrogenated carbon nitride films
Authors: Camero, M ×
Buijnsters, Josephus Gerardus
Gomez-Aleixandre, C
Gago, R
Caretti, I
Jimenez, I #
Issue Date: Mar-2007
Publisher: American Institute of Physics
Series Title: Journal of Applied Physics vol:101 issue:6 pages:063515-1-063515-7
Abstract: This work describes the composition and bonding structure of hydrogenated carbon nitride (a-CNx:H) films synthesized by electron cyclotron resonance chemical vapor deposition using as precursor gases argon, methane, and nitrogen. The composition of the films was derived from Rutherford backscattering and elastic recoil detection analysis and the bonding structure was examined by infrared (IR) spectroscopy and x-ray absorption near edge spectroscopy (XANES). By varying the nitrogen to methane ratio in the applied gas mixture, polymeric a-CNx:H films with N/C contents varying from 0.06 to 0.49 were obtained. Remarkably, the H content of the films (similar to 40 at. %) was rather unaffected by the nitrogenation process. The different bonding states as detected in the measured XANES C(1s) and N(1s) spectra have been correlated with those of a large number of reference samples. The XANES and IR spectroscopy results indicate that N atoms are efficiently incorporated into the amorphous carbon network and can be found in different bonding environments, such as pyridinelike, graphitelike, nitrilelike, and amino groups. The nitrogenation of the films results in the formation of N-H bonding environments at the cost of C-H structures. Also, the insertion of N induces a higher fraction of double bonds in the structure at the expense of the linear polymerlike chains, hence resulting in a more cross-linked solid. The formation of double bonds takes place through complex C=N structures and not by formation of graphitic aromatic rings. Also, the mechanical and tribological properties (hardness, friction, and wear) of the films have been studied as a function of the nitrogen content. Despite the major modifications in the bonding structure with nitrogen uptake, no significant changes in these properties are observed. (c) 2007 American Institute of Physics.
ISSN: 0021-8979
Publication status: published
KU Leuven publication type: IT
Appears in Collections:Department of Materials Engineering - miscellaneous
× corresponding author
# (joint) last author

Files in This Item:
File Description Status SizeFormat
pub05554.pdfMain article Published 148KbAdobe PDFView/Open Request a copy

These files are only available to some KU Leuven Association staff members


All items in Lirias are protected by copyright, with all rights reserved.

© Web of science